Ukraine, Krivoy Rog

5 Kolomoytsevskaya str.

Tel. +38 (097) 580 73 44 

e-mail: This email address is being protected from spambots. You need JavaScript enabled to view it.      

Kazakhstan, Kostanay

95 Baitursynov str, of. 420

Tel. +7 777 446 45 84

e-mail: This email address is being protected from spambots. You need JavaScript enabled to view it.      

Russia, Stary Oskol

18 md. East, of. 4

Tel. +7 906 565 98 35

e-mail: This email address is being protected from spambots. You need JavaScript enabled to view it.      

Silicate-manganese ceramics

    Products made of manganese silicate-ceramics exhibit wear resistance, heat resistance and resistance to acids, to their strength properties correspond to the oncrete of 550-700 brands retain physical properties at temperatures up to 1150 ° C.

    Silicate-manganese ceramics successfully replaces basalt casting refractory materials, concrete, as well as to protect steel structures against heat, abrasion and corrosion.

    Product: plate raw and machined, pipe lining, customer drawings

    Physical and mechanical properties:

• Bulk weight - 2.9 t / m3;

 • Tensile strength - at least 30 MPa;

• Abrasion - not more than 0.02 g / m2;

• Thermal stability - up to 1150 ° C;

• Water absorption - less than 1%.

Product: untreated plates, plates machined, lining pipe and other products according to customer drawings.

Carrying out industrial tests showed that the lining silicate-manganese ceramics increases the service life of pipes and turning 5 times!

Comparative characteristics of physical and chemical indicators of manganese silicate ceramics (MSC) and cast stone (basalt)

#

Physical and chemical parameters

Averages

MSC

Basalt

1

Chemical composition :

 

 

 - SiO2, %

49,50

49,06

 - MnO, %

11,00

0,31

2

Density, kg / m3

3 000,00

2 950,00

3

Abrasion g / cm2

0,014

0,500

4

Thermal resistance, C

Up to1150

Up to 1050

5

Water absorption g / cm2

0,57

5,20

6

Compressive strength, MPa

206,50

200,00

7

The ultimate strength in static bending, MPa

48,00

40,00

8

The total specific activity of natural radionuclides, Bq / kg

132,00

 -

9

Frost, the number of cycles (at least)

150,00

 -

10

Loss of strength,%

2,70

 -

11

Chemical resistance

Products are chemically resistant to hydrochloric acid (HCl) and potassium hydroxide (KOH)